E130i is a LCP grade from Celanese, regularly exported by Ningbo Xianxunhe New Materials. Typical characteristics: Glass fiber reinforced · Flame retardant · Heat resistant · High flow. Typical applications: SMT connector, SIM socket, fine pitch part.
Key typical values of E130i: density 1.61 g/cm³ · and tensile strength 165 MPa. All figures are manufacturer typical values for material selection reference — request the original TDS/COA before using them as purchase specifications.
We supply E130i on FOB Ningbo terms with a 1-ton MOQ and free samples (0.5–2 kg) for lab validation. In-stock grades are dispatched within 48 hours.
| Density | 1.61 g/cm³ | ASTM D792 / ISO 1183 | |
|---|---|---|---|
| Water absorption | 0.02 % | ASTM D570 / ISO 62 |
| Tensile strength | 165 MPa | ASTM D638 / ISO 527 | |
|---|---|---|---|
| Elongation at break | 3 % | ASTM D638 / ISO 527 | |
| Flexural modulus | 15000 MPa | ASTM D790 / ISO 178 | |
| Flexural strength | 210 MPa | ASTM D790 / ISO 178 | |
| Izod impact, notched | 12 kJ/m² | ASTM D256 / ISO 180 | |
| Charpy impact | 14 kJ/m² | ISO 179 | |
| Hardness | R 110 | ASTM D785 |
| HDT (0.45 MPa) | 280 °C | ASTM D648 / ISO 75 | |
|---|---|---|---|
| Vicat softening point | 290 °C | ASTM D1525 / ISO 306 | |
| Melting point | 335 °C | ISO 11357 |
Values above are industry-typical starting points — fine-tune according to part geometry, wall thickness and equipment.
E130i has a typical density of 1.61 g/cm³ (ISO 1183).
The tensile strength of E130i is 165 MPa (ISO 527).
The notched impact strength of E130i is approximately 12 kJ/m² (ISO 180/179).
The HDT of E130i (1.8 MPa, unannealed) is 280 °C (ISO 75).
The Vicat softening temperature of E130i is 290 °C (ISO 306).
E130i is produced by Celanese (origin: USA). Xianxunhe supplies it as a trading partner with complete export documentation (COA, TDS on request).
Typical applications of E130i: SMT connector, SIM socket, fine pitch part.
MOQ is 1 ton, FOB Ningbo. In-stock grades dispatch within 24–48 hours; free samples (0.5–2 kg) are available for testing.
Datasheet values are compiled from manufacturer data sheets and third-party test reports, for reference only and without warranty of any kind. Please request the official TDS/COA from the manufacturer and test sufficiently before material selection. The COA of the shipped lot prevails.. Note: MFR test conditions may differ between grades and manufacturers, so MFR values are not directly comparable.