B30S is a PA6 grade from BASF, regularly exported by Ningbo Xianxunhe New Materials. Typical characteristics: High flow · High stiffness. Typical applications: Fastener, clip, connector, thin-wall part.
Key typical values of B30S: density 1.13 g/cm³ · and tensile strength 82 MPa. All figures are manufacturer typical values for material selection reference — request the original TDS/COA before using them as purchase specifications.
We supply B30S on FOB Ningbo terms with a 1-ton MOQ and free samples (0.5–2 kg) for lab validation. In-stock grades are dispatched within 48 hours.
| Density | 1.13 g/cm³ | ASTM D792 / ISO 1183 | |
|---|---|---|---|
| Water absorption | 1.8 % | ASTM D570 / ISO 62 |
| Tensile strength | 82 MPa | ASTM D638 / ISO 527 | |
|---|---|---|---|
| Elongation at break | 90 % | ASTM D638 / ISO 527 | |
| Flexural modulus | 3100 MPa | ASTM D790 / ISO 178 | |
| Flexural strength | 125 MPa | ASTM D790 / ISO 178 | |
| Izod impact, notched | 5 kJ/m² | ASTM D256 / ISO 180 | |
| Charpy impact | 6.5 kJ/m² | ISO 179 | |
| Hardness | R 122 | ASTM D785 |
| HDT (0.45 MPa) | 78 °C | ASTM D648 / ISO 75 | |
|---|---|---|---|
| Vicat softening point | 210 °C | ASTM D1525 / ISO 306 | |
| Melting point | 221 °C | ISO 11357 |
⚠ Hygroscopic material — drying is mandatory; residual moisture causes hydrolytic degradation and silver streaks.
Values above are industry-typical starting points — fine-tune according to part geometry, wall thickness and equipment.
B30S has a typical density of 1.13 g/cm³ (ISO 1183).
The tensile strength of B30S is 82 MPa (ISO 527).
The notched impact strength of B30S is approximately 5 kJ/m² (ISO 180/179).
The HDT of B30S (1.8 MPa, unannealed) is 78 °C (ISO 75).
The Vicat softening temperature of B30S is 210 °C (ISO 306).
B30S is produced by BASF (origin: Germany). Xianxunhe supplies it as a trading partner with complete export documentation (COA, TDS on request).
Typical applications of B30S: Fastener, clip, connector, thin-wall part.
MOQ is 1 ton, FOB Ningbo. In-stock grades dispatch within 24–48 hours; free samples (0.5–2 kg) are available for testing.
Datasheet values are compiled from manufacturer data sheets and third-party test reports, for reference only and without warranty of any kind. Please request the official TDS/COA from the manufacturer and test sufficiently before material selection. The COA of the shipped lot prevails.. Note: MFR test conditions may differ between grades and manufacturers, so MFR values are not directly comparable.
Tell us the resin, grade and quantity — we reply with a formal quotation within 12 hours.